Trimethylethoxysilane (TMES) has been recognized as a good co-precursor to increase the degree of hydrophobicity during the synthesis of a silica aerogel because of its methyl groups. Therefore, some physical properties of silica aerogels, including the contact angle and porosity, were investigated using TMES as a co-precursor at different molar ratios with the main precursor such as tetramethoxysilane (TMOS) or tetraethoxysilane (TEOS). In contrast to TMES, most silylating agents such as hexamethyldisilazane (HMDZ) and trimethylchlorosilane (TMCS) have been used for surface modification because of their ability to enhance the hydrophobicity of the aerogel surface. This work examines the silylation effect, which includes increasing hydrophobicity by TMES to determine the possibility of using it as an alternative silylating agent during ambient pressure drying in the synthesis of sodium silicate-based silica aerogel. In addition, the physical properties of sodium silicate-based silica aerogels with silylation under different TMES/TMCS volume ratio are investigated. The physical properties of sodium silicate-based aerogels can be changed by the TMES/TMCS volume ratio during the surface modification step. Aerogels with a high specific surface area (458 m2/g), pore volume (3.215 cm3/g), porosity (92.7%), and contact angle (131.8°) can be obtained TMES/TMCS volume ratio of 40/60.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.