Abstract
In this paper, the Ti6Al4V alloy surface was modified via ceramic conversion treatment (CCT) with or without a pre-deposited silver layer. After characterizing the surface morphologies, microstructure and phase constituents of the ceramic oxide layer formed at 620 °C, we investigated the surface hardness and the cross-sectional nano-hardness profile under the oxide layer. The static load-bearing capacity of the oxide layers was examined by applying discrete loads via a Vickers indenter and observing the indentations. A scratch test was used to evaluate the load-bearing capacity and the adhesion/cohesion of the oxide layers. The wettability of the surface changed due to the incorporation of silver and the change of surface morphology. Reciprocating friction and wear test was used to assess the tribological properties. Small and dispersed silver nanoparticles and clusters were found in the oxide layer of the Ag pre-deposited Ti6Al4V samples, and they had much better tribological properties in terms of reduced coefficient of friction and wear volume. With the assistance of silver, the efficiency of the CCT was significantly improved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.