Silver nanoparticles induce cytotoxicity, but not cell transformation or genotoxicity on Balb3T3 mouse fibroblasts

Abstract

AbstractSilver nanoparticles (Ag NPs) are one of the most common nanomaterials present in nanotechnology-based products. Here, the physical chemical properties of Ag NPs suspensions of 44 nm, 84 nm and 100 nm sizes synthesized in our laboratory were characterized. The NM-300 material (average size of 17 nm), supplied by the Joint Research Centre Nanomaterials Repository was also included in the present study. The Ag NPs potential cytotoxicity was tested on the Balb3T3 cell line by the Colony Forming Efficiency assay, while their potential morphological neoplastic transformation and genotoxicity were tested by the Cell Transformation Assay and the micronucleus test, respectively. After 24 h of exposure, NM-300 showed cytotoxicity with an IC50 of 8 µM (corresponding to 0.88 µg/mL) while for the other nanomaterials tested, values of IC50 were higher than 10 µM (1.10 µg/mL). After 72 h of exposure, Ag NPs showed size-dependent cytotoxic effect with IC50 values of 1.5 µM (1.16 µg/mL) for NM-300, 1.7 µM (1.19 µg/mL) for Ag 44 nm, 1.9 µM (0.21 µg/mL) for Ag 84 nm and 3.2 µM (0.35 µg/mL) for Ag 100 nm. None of the Ag NPs tested was able to induce either morphological neoplastic transformation or micronuclei formation.