Abstract
Highly dispersed silicotungstic acid-derived WO3 composited with ZrO2 supported on SBA-15 (WZ/SBA-15) as an ordered mesoporous solid acid catalyst was prepared via a facile incipient wetness impregnation (IWI) method that active ingredients, ZrO2 and WO3, were impregnated into the channels of SBA-15 simultaneously with a subsequent calcination process. The relationship between catalyst nature and performance was explored by high resolution transmission electron microscopy (HRTEM), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), FT-IR, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), N2 adsorption-desorption, NH3 temperature-programmed desorption (NH3-TPD), and FT-IR of pyridine adsorption (Py-IR) characterization techniques. The catalytic performance of W12Z15/SBA-15 is not only greater than that of single component solid acid catalysts, WO3/SBA-15 and ZrO2/SBA-15, but also W12/Z15/SBA-15 prepared by impregnating active ingredients, ZrO2 and WO3, into SBA-15 in sequence. The outstanding performance of W12Z15/SBA-15 is derived from the strong interaction between ZrO2 and WO3, which results in more acid sites, and relatively high specific surface area, large pore volume, and ordered mesoporous structure of SBA-15. The characterization and reaction results clearly demonstrate that the synergy of ZrO2 and WO3 has a clear boost for the alkenylation. The optimized W12Z15/SBA-15-500 achieves a 99.4% conversion of phenylacetylene and a 92.3% selectivity of main product α-arylstyrene for the alkenylation of p-xylene with phenylacetylene, with very low level of oligomers producing at the same time. Moreover, W12Z15/SBA-15-500 shows excellent catalytic stability and regeneration. Therefore, W12Z15/SBA-15-500 is a promising solid acid catalyst for the alkenylation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.