Abstract
Silicon carbide (SiC) whisker reinforced SiC ceramic matrix composites were prepared by chemical vapor infiltration. Microstructure and mechanical properties of the composites were investigated. The fracture toughness of the composites was improved to 5.65–7.21 MPa m 1/2, and its flexural strength value was between 196 MPa and 305 MPa, depending on the relative density. The pullout of rough whisker, crack deflection and whisker bridging are responsible for the improvement in fracture toughness. The randomly oriented whiskers that paralleled to the crack plane, and the weak bonding strength between whisker and matrix could not have much stress transfer from the matrix, leading to the low flexural strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.