Abstract
The composition and chemical bonding of the first atoms across the interface between Si(001) and the dielectric determine the quality of dielectric gate stacks. An analysis of that hidden interface is a challenge as it requires both, high sensitivity and elemental and chemical state information. We used X-ray absorption spectroscopy in total electron yield and total fluorescence yield at the Si2p and the O1s edges to address that issue. We report on results of Pr 2O 3/Si(001) as prepared by both, epitaxial growth and metal organic chemical vapor deposition (MOCVD), and compare to the SiO 2/Si(001) system as a reference. We find evidence for the silicate formation at the interface as derived from the characteristic features at the Si2p and the O1s edges. The results are in line with model experiments in which films of increasing film thickness are deposited in situ on bare Si(001) surfaces.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.