Abstract
Abstract An evaluation of the fibre/matrix interfacial shear strength was performed by the single-fibre fragmentation tests on polypropylene–glass fibre microcomposites filled with various types and amounts of silica nanoparticles. In particular, both non-functionalized and dimethyldichlorosilane-functionalized silica nanoparticles were added up to a weight content of 7%. Moreover, the effect of various amounts of maleic anhydride modified polypropylene (PPgMA) on the fibre/matrix adhesion was also investigated, including some selected formulations containing both PPgMA and silica nanoparticles. Interfacial shear strength was found to remarkably increase (up to a factor of about 5 for a 7 wt% content of surface treated nanoparticles) with respect to the case of neat polypropylene matrix. The observed effect was explained by considering that silica nanoparticles increase the work of adhesion of polypropylene with respect to glass, as proven by contact angle measurements in different liquids. In addition, silica nanoparticles promoted a remarkable enhancement of both elastic modulus and creep stability of the selected polypropylene matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.