Abstract
The present work strives to evaluate the corrosion resistance of aluminum alloy (AA)6061-T6 (UNS A96061) pretreated with bis-1,2-[triethoxysiyl]ethane silane (BTSE) solution containing different contents of yttrium oxide (Y2O3) nanoparticles. The corrosion resistance of the pretreated AA6061-T6 substrates was investigated with potentiodynamic polarization curves and the neutral salt spray (NSS) test. The morphologies of the silane film were observed using scanning electron microscopy (SEM). The results indicated that the presence of small amounts of Y2O3 nanoparticles in BTSE solutions can increase the corrosion resistance of the silane films in 3.5% sodium chloride (NaCl) solution. Y2O3 nanoparticles do not change the behavior of the electrode reaction. The formed silane film acts as a physical barrier for the protection of aluminum alloy. The SEM images indicated that the surface morphologies of silane films formed were flat and compact, when the contents of the Y2O3 nanoparticles in BTSE solutions were between 10 ppm and 20 ppm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.