Abstract
We have fabricated graphene nanoplate (GNP) incorporated Cu2Se using ball milling followed by a spark plasma sintering (SPS) process. All samples have been characterized comprehensively by high resolution transmission electron microscopy, room temperature and high temperature synchrotron X-ray diffraction, differential thermal analysis, and thermoelectric properties measurements. The GNP was found to be densely and homogeneously distributed inside the matrix material, leading to a large density of grain boundaries and refined Cu2Se grains as well as GNP/Cu2Se interfaces. Despite only slight changes to the electrical conductivity, Seebeck coefficient, and power factor as a result of the GNP incorporation, the figure-of-merit (zT) in GNP incorporated Cu2Se was enhanced by a factor of up to 1.7 at 873 K compared to the undoped sample. Our results indicate that it is the GNP/Cu2Se interfaces that play an important role in the great reduction of thermal conductivity and significantly enhancement of zT. This work provides a suitable strategy to apply carbon engineering to improve thermoelectric performance in the Cu2Se and other related compounds.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.