Abstract
The oxidation behaviour of Cf/ZrB2-SiC with different fibre architectures, manufactured by slurry impregnation, polymer infiltration and mild pyrolysis, was investigated. Short term oxidation tests in air were performed for 1 min and 5 min at 1500 °C and 1650 °C in a bottom loading furnace. Microstructure, oxide scale thickness and composition were analysed by SEM/EDS/XRD. Results indicated that a good dispersion of ZrB2 particles in the polymer derived SiC(O) matrix promoted the formation of compact scales filling surface holes left by fibre oxidation. 20−30 vol% of ZrB2 in the material was found a good compromise between lightness and oxidation resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.