Abstract
Accumulative roll bonding (ARB) process was used in this study as an effective method for manufacturing high-strength, finely-dispersed and highly-uniform A356 alloy. It was found that when the number of ARB cycles was increased, the uniformity of silicon particles in the aluminum matrix improved, the particles became finer and spheroider and therefore, the tensile strength (TS) and ductility of the samples improved. The microstructure of the manufactured A356 alloy after five ARB cycles indicated a totally modified structure such that it's TS and elongation values reached 269MPa and 5.3% which were 2.6 and 2.5 times greater than those of the as-cast material, respectively. Also, the hardness value increased from 55.4 (for as-cast sample) to 100.2HV (after the fifth cycle of ARB), and registered 81% increase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.