Abstract
Abstract An overall lamellar-type nanostructure was successfully obtained in maraging steel via equal-channel angular pressing (ECAP) for 12 passes at room temperature. After subsequent ageing treatment (440–500 °C), the nano-thick martensite lamellae still survived, while the high density nano-precipitates emerged within them uniformly. By ECAP and subsequent aging treatment, very high tensile strength (2400–2700 MPa) was achieved in comparison with the general strength of 1985 MPa. The influences of ECAP and aging treatment on the microstructures and tensile strength were discussed qualitatively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.