Abstract
The signal performances of YBa 2Cu 3O 7− δ (YBCO) direct current superconducting quantum interference devices (DC-SQUIDs) have been investigated as a function of the thin film structure affected by the growth process. YBCO thin films of 200 nm thicknesses were deposited by DC magnetron sputtering using different deposition rates between 1.0 nm/min and 2.0 nm/min onto 24° bicrystal SrTiO 3 (STO) substrates. The thin film samples were subsequently analyzed by XRD and AFM in order to determine their crystalline structures and surface morphologies respectively. The 67 pH directly coupled DC-SQUIDs with 4 μm-wide bicrystal Josephson junctions were fabricated, and characterized with respect to their device performances. The variations in the critical current ( I c), the voltage modulation depth (Δ V) and the noise performance of DC-SQUIDs were reported. The SQUIDs having relatively low deposition rate of 1.0 nm/min was observed to have larger voltage modulation depth as well as higher critical current than that of the samples having larger rate of 2.0 nm/min. The better noise performances were observed as the film deposition rate decreases. The results were associated with the thin film structure and the SQUID characteristics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.