Abstract
Ni(Cr1-xAlx)2O4 (x=0–0.50) samples were prepared in single phase form by using sol-gel method and their structural and magnetic properties were studied. Al substitution transforms the crystal structure of NiCr2O4 from tetragonal cell with space group I41/amd to cubic cell of Fd3¯m space group. Magnetization measurements by varying the temperature and magnetic field were carried out to investigate the interesting magnetization reversal and exchange bias behaviors. Magnetization reversal is observed for x=0.10 sample with a magnetic compensation temperature of 40K and it is explained by considering different temperature dependences of magnetic moments of the two sublattices. Shifting of magnetic hysteresis loops towards the negative magnetic field axis and hence the presence of negative exchange bias field is observed for x=0.15 sample. The x=0.10 sample exhibits the tunable positive and negative exchange bias field. Exchange bias in these samples is explained considering the anisotropic exchange interaction between the ferrimagnetic and the antiferromagnetic components of magnetic spins. However, the sign reversal of exchange bias field is due to the change in domination of one ferrimagnetic sublattice over the other with variation in temperature. Both normal and inverse magnetocaloric effects are observed for x=0.10 sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.