SiGe pMODFETs on silicon-on-sapphire substrates with 116 GHz f/sub max/

Abstract

The dc and microwave results of Si/sub 0.2/Ge/sub 0.8//Si/sub 0.7/Ge/sub 0.3/ pMODFETs grown on silicon-on-sapphire (SOS) substrates by ultrahigh vacuum chemical vapor deposition are reported. Devices with L/sub g/=0.1 μm displayed high transconductance (377 mS/mm), low output conductance (25 mS/mm), and high gate-to-drain breakdown voltage (4 V). The dc current-voltage (I-V) characteristics were also nearly identical to those of control devices grown on bulk Si substrates. Microwave characterization of 0.1×50 μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> devices yielded unity current gain (f <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">T</sub> ) and unilateral power gain (f <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">max</sub> ) cutoff frequencies as high as 50 GHz and 116 GHz, respectively. Noise parameter characterization of 0.1×90 μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> devices revealed minimum noise figure (F <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">min</sub> ) of 0.6 dB at 3 GHz and 2.5 dB at 20 GHz.