Side-hole to anti-hole conversion in time-resolved spectral hole burning of ruby: Long-lived spectral holes due to ground state level population storage

Abstract

We report time-resolved transient spectral hole burning of Verneuil-grown 20 ppm and ca. 0.6 ppm ruby (Al 2O 3:Cr 3+) in zero field and low magnetic fields B∥ c at 4 K. The hole-burning spectroscopy of the 20 ppm sample implies relatively rapid cross relaxation in the 4A 2 ground state on the ∼1 ms timescale both in zero field and in low magnetic fields, B∥ c, up to 0.2 T. In the 0.6 ppm sample, side-hole to anti-hole conversion is observed both in zero field and in low magnetic fields. This conversion is caused by population storage in 4A 2 ground state levels. Spin-lattice relaxation, on the 200 ms timescale, is directly observed from the time dependence of the resonant hole and anti holes in B∥ c, consistent with a very low cross-relaxation rate. However, in zero field cross relaxation in the 4A 2 ground state is still a significant relaxation mechanism for the 0.6 ppm sample resulting in hole decay in ∼50 ms.