Abstract
ABSTRACTThe kinetics of short crack growth has been studied in austenitic‐ferritic 2205 duplex stainless steel. Smooth cylindrical specimens and specimens with shallow notch were subjected to constant plastic strain amplitude loading. The crack growth was studied in notched specimens. The notch area has been mechanically and electrolytically polished to facilitate the observation of crack initiation and growth. The initiated cracks were observed in an SEM (scanning electron microscope). The crack growth was studied using long distance QUESTAR optical microscope equipped with high‐resolution camera. In constant plastic strain amplitude loading the microcracks were initiated and their growth kinetics has been studied. The characteristic features of the crack growth at different plastic strain amplitudes were recorded. Two approaches to analyse the crack growth rates were adopted. The comparison of the prediction of the fatigue life using the plastic‐strain‐dependent crack growth rate was compared with Manson–Coffin law and the relation between parameters of this law and parameters of the short crack growth law were established.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.