Abstract
The purpose of this research was to systematically study the influence of peak-shock pressure and second-phase reinforcement on the structure/property response of shock-loaded 6061-T6 Al-alumina composites. The reload stress-strain response of monolithic 6061-T6 Al, used as a baseline for comparison, showed no increased shock hardening compared to the unshocked material deformed to an equivalent strain. The reload stress-strain response of the shock-loaded 6061-T6 Al-alumina composites exhibited a lower reload yield strength than the flow stress of the starting composites. The degree of strength loss was found to increase with increasing shock pressure. Wavespeed measurements of shock-prestrained specimens showed no degradation compared to unshocked specimens, indicating that particle cracking had not occurred under shock. This result was supported by optical metallography, which did not reveal cracked particles or particle decohesion in the shock-prestrained samples. The reload stress-strain response of the shock-prestrained composites, after resolutionizing and T6 reaging, showed that the composites recovered their full as-received preshock stress-strain responses. This result supports the finding that degradation in reload strength was attributable to matrix microstructural changes resulting from the shock. Transmission electron microscopy (TEM) examination of the shock-loaded microstructures revealed that the matrix regions adjacent to the particle/matrix interface had undergone significant recovery and partial recrystallization resulting from the shock. This type of near-interface substructure is in stark contrast to the heavily dislocated near-interface dislocation substructure of the as-received composites. The loss of dislocation density(i.e., strain hardening) in the near-interface matrix region, resulting from the shock, highlights the importance of the thermally introduced dislocation substructure changes in establishing the strength of metal-matrix composites (MMCs).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.