Abstract
Although fiber-reinforced composites (FRC) are now available for use as orthodontic retainers, little is known about their bonding properties. Our aim in this study was to investigate the adhesive properties of various composites to a commercially available FRC retainer. Five flowable composites (Grandio Flow [Voco GmbH, Cuxhaven, Germany], Synergy Flow [Coltène/Whaledent AG, Genf, Switzerland], Tetric Flow [Ivoclar Vivadent AG, Schaan Fürstentum, Liechtenstein], Tetric Flow Chroma [Ivoclar Vivadent AG], and Transbond LR [3M Unitek, Monrovia, Calif) were tested for their shear bond strengths to the EverStick Ortho (Stick Tech Ltd Oy, Turku, Finland) FRC retainer stick. Each group contained 15 samples and underwent 1000 aging cycles between 5 degrees C and 55 degrees C. A testing machine was used to measure the shear bond strengths at the composite-FRC interface. All specimens were visually controlled for the location of the fracture line. Typical shear bond strengths were measured at 40 N or 8 MPa. No significant difference was found between the 5 composites (ANOVA, P < or = 0.05). The fracture line was consistently in the FRC retainer. All composites had similar bonding characteristics, and visual inspection consistently showed fractures in the FRC retainer. Because the point of least resistance was in the retainer, we concluded that all tested composites were equally effective.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: American Journal of Orthodontics and Dentofacial Orthopedics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.