Abstract
Hierarchical and hexagonal cobalt oxide with porous structure was synthesized via a precipitation route followed by calcination. The shape and crystal size of cobalt oxide were greatly dependent on the chemicals and calcination temperature. The as-synthesized cobalt oxide reserved the shape of its hydroxide precursor. The calcination temperature was a key factor for controlling the pore volume and crystal sizes of as-prepared Co3O4 samples. The cobalt oxide prepared under different conditions was characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and nitrogen physisorption analysis. The gas-sensing properties were measured by a gas sensor measurement system using Co3O4 samples as a sensor material. The influence of gas concentrations, specific surface area and crystals size of Co3O4 on sensing properties were investigated. The porous hierarchical cobalt oxide with a small crystal size and high surface area showed a high response to ethanol vapor, while cobalt oxide platelets with a large crystal size and macropore exhibited a high response to acetone vapor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.