Abstract
Under neutron irradiation, radiation enhanced beta-Nb nano-precipitates develop within the α-grains of the Zr-Nb alloys. This radiation enhanced precipitation is of great interest since it may have some influence on the post-irradiation mechanical behavior of the material. In this paper the shape, the orientation relationship and the interface structure of such nano-particles are studied by means of both conventional and high-resolution transmission electron microscopy. The radiation damage was annealed out, thanks to a prior heat treatment and a creep test, in order to easily observe the beta-Nb nano-particles. The nano-particles exhibit a needle-like shape with a short thickness along the c-direction of 1.5 nm on average, a length and a width respectively of 6 nm and 3 nm, on average, in the basal plane. Using high-resolution TEM, a near Pitsch-Schrader orientation relationship is identified for a nano-particle. The interface atomic structure at various locations around the nano-particle has been accurately determined and an atomic model of the interface structure has been proposed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.