Abstract
ABSTRACTCarboxylated‐terminated liquid acrylonitrile rubber (CTBN) and epoxy resin (JEF‐0211) were coreacted with cyanate ester (CE) to form CTBN/EP/CE ternary resin systems. Further, the ternary resin system was applied as prepreg for carbon fiber composites with vacuum bag degassing molding process. CTBN/EP/CE ternary shape memory polymer (SMP) exhibited relatively high tensile strength, Young's modulus, impact strength, and excellent shape memory properties. Compared with CTBN/EP/CE ternary SMP, CTBN/EP/CE carbon fiber composites showed much higher mechanical properties, such as their tensile strength and Young's modulus were high to 570 MPa and 36.7 GPa, respectively. Furthermore, CTBN/EP/CE carbon fiber composites exhibited good shape memory properties, their shape fixity ratio and shape recovery ratio were more than 95% after 30 times repeating shape memory tests. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48756.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.