Abstract
Different kinds of diffusion processes, plasma nitriding, oxidizing and oxynitriding as of a combination of other two, have been applied to Ti6Al4V alloy to evaluate the effect of treatment times (1 and 4 h) and temperatures (650 and 750 °C) on wear properties of the alloy. It was observed that a hard modified layer was produced on the surface of the alloy after each diffusion process. While TiN and Ti 2N phases form in the modified layer with plasma nitriding, mainly TiO 2 phase forms after plasma oxidizing treatment. The wear tests performed at different normal loads showed that all treated samples, except for nitrided and oxidized at 650 °C for 1 h, exhibited higher wear resistance than untreated Ti6Al4V alloy. The plasma nitrided samples showed adhesive wear. On the other hand, while the plasma oxidizing samples displayed adhesive wear at lower loads, wear mechanism changed to abrasive wear as the load increased because the oxide film which covers the surface was broken during the sliding at higher loads.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.