Abstract
AbstractIn this paper, setting time, strength and bond of high-calcium fly ash geopolymer concrete were investigated. The high-calcium fly ash was from Mae Moh power plant in northern Thailand. Both sodium silicate solution and sodium hydroxide solution were used as alkali activators in every mix. Sodium hydroxide solution with 10 M, 15 M, and 20 M concentrations, sodium silicate to sodium hydroxide ratios of 1.0 and 2.0, alkaline liquid to fly ash ratio of 0.5 and two curing regimes viz., heat curing at 60±2°C for 24 h and room temperature curing at 23±2°C were used. The results indicated that fresh geopolymer concrete had short setting time of 28–58 min due to the presence of high calcium content of fly ash. In general, strengths and modulus of elasticity increased with the increase in NaOH concentration. For compressive strength, the optimum Na2O content was around 12% of fly ash. The high-strength geopolymer concrete with 28-day compressive strength of 54.4 MPa was obtained for mix with 15M NaOH. The ...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.