Abstract
Calcium oxide (CaO) slurry mixed with water hardens and expands by hydration. The authors used this setting characteristic as a binder of zirconia-refractory investments. If a mixed slurry was placed in air, unreacted residual calcia powders absorbed water and reverted to calcium hydroxide (Ca (OH)2). This resulted in a large setting expansion that continued for several days. A carbon dioxide (CO2) gas atmosphere controlled this expansion of calcia. When mixed slurry was placed in a carbon dioxide gas atmosphere, calcium carbonate (CaCO3) was formed and prevented the further hydration of unreacted calcium oxide. Thus setting expansion values were controlled. The combined expansion of setting and thermal expansion, in CaO-CO2-bonded zirconia investments, was about 1.5-2.5%. On the whole, calcium oxide is expected to be a good binder for high temperature dental casting refractory.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japanese Society for Dental Materials and Devices
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.