Semiconducting ZnSnN2 thin films for Si/ZnSnN2 p-n junctions

Abstract

ZnSnN2 is regarded as a promising photovoltaic absorber candidate due to earth-abundance, non-toxicity, and high absorption coefficient. However, it is still a great challenge to synthesize ZnSnN2 films with a low electron concentration, in order to promote the applications of ZnSnN2 as the core active layer in optoelectronic devices. In this work, polycrystalline and high resistance ZnSnN2 films were fabricated by magnetron sputtering technique, then semiconducting films were achieved after post-annealing, and finally Si/ZnSnN2 p-n junctions were constructed. The electron concentration and Hall mobility were enhanced from 2.77 × 1017 to 6.78 × 1017 cm−3 and from 0.37 to 2.07 cm2 V−1 s−1, corresponding to the annealing temperature from 200 to 350 °C. After annealing at 300 °C, the p-n junction exhibited the optimum rectifying characteristics, with a forward-to-reverse ratio over 103. The achievement of this ZnSnN2-based p-n junction makes an opening step forward to realize the practical application of the ZnSnN2 material. In addition, the nonideal behaviors of the p-n junctions under both positive and negative voltages are discussed, in hope of suggesting some ideas to further improve the rectifying characteristics.