Thick and crack-free semi-polar (11-22) AlGaN layers with various high Al compositions have been achieved by means of growth on the top of nearly but not yet fully coalesced GaN overgrown on micro-rod templates. The range of the Al composition of up to 55.7% was achieved, corresponding to an emission wavelength of up to 270 nm characterised by photoluminescence at room temperature. X-ray diffraction (XRD) measurements show greatly improved crystal quality as a result of lateral overgrowth compared to the AlGaN counterparts on standard planar substrates. The full width at half maximums of the XRD rocking curves measured along the [1-100]/[11-2-3] directions (the two typical orientations for characterizing the crystal quality of (11-22) AlGaN) are 0.2923°/0.2006° for 37.8% Al and 0.3825°/0.2064° for 55.7% Al, respectively, which have never been achieved previously. Our calculation based on reciprocal space mapping measurements has demonstrated significant strain relaxation in the AlGaN as a result of utilising the non-coalesced GaN underneath, contributing to the elimination of any cracks. The results presented have demonstrated that our overgrowth technique can effectively manage strain and improve crystal quality simultaneously.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.