Abstract
Few‐layer graphene oxide (GO) is assembled on the silicon surface by a self‐assembly approach via covalent interaction using 3‐aminopropyltrimethoxysilane (APTMS) as a bifunctional chemical linker. X‐ray photoelectron spectroscopy results suggest chemical interactions between oxygen functionalities of GO and amino group of APTMS thin film. The oxygen functionalities of GO thin film are eliminated by vacuum ultraviolet (VUV) photon exposure. Topographic images reveal efficient grafting of GO on the silicon and suggest the presence of few layers in the GO thin film along with wrinkles and folds. Microtribological properties of VUV‐reduced GO (rGO) thin film are probed under the mean contact pressure of 0.3–0.6 GPa. The rGO thin film exhibits low and steady friction (0.12–0.15) compared to that of bare silicon (0.6). The rGO thin film could survive for ≈37 000 laps at 100 mN load, revealing its remarkable wear‐resistivity. Microscopic images and carbon mapping reveal the deposition of delaminated graphene lamellae on the counter steel ball surface. The low friction and excellent wear‐resistivity of rGO thin film are collectively attributed to low‐resistance to shear between the neighboring lamellae of rGO, full coverage and strong interaction of rGO thin film with silicon, and deposition of delaminated graphene lamellae on the counter steel surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.