Abstract
The growth of Fe nanoclusters on the Ge(001) and MoO2/Mo(110) surfaces has been studied using low-temperature scanning tunneling microscopy (STM) and X-ray magnetic circular dichroism (XMCD). STM results indicate that at low coverage Fe atoms self-assemble on both surfaces into well-separated nanoclusters, which nucleate at equivalent surface sites. Their size, shape, and the observed spatial separation are dictated by the substrate and depend on preparation conditions. Annealing the Fe nanoclusters on Ge(001) at 420 K leads to the formation of linear nanocluster arrays, which follow the Ge dimer rows of the substrate, due to cluster mobility at such temperature. In turn, linear Fe nanocluster arrays are formed on the MoO2/Mo(110) surface at room temperature at a surface coverage greater than 0.5 monolayer. This is due to the more pronounced row pattern of the MoO2/Mo(110) surface compared to Ge(001). These nanocluster arrays follow the direction of the oxide rows of the strained MoO2/Mo(110) surface. The Fe nanoclusters formed on both surfaces show a superparamagnetic behavior as measured by XMCD.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.