Self-Assembled GaN Nano-Column Grown on Si(111) Substrate Using Au+Ga Alloy Seeding Method by Metalorganic Chemical Vapor Deposition

Abstract

Single-crystal GaN nano-column arrays were grown on Au-coated silicon (111) substrate by Au-Ga alloy seeding method using metalorganic chemical vapor deposition (MOCVD). The nano-column arrays were studied as a function of growth parameters and Au thin film thickness. The diameter and length of the as-grown nano-column vary from 100 to 500 nm and 4 to 6 µm, respectively. The surface morphology and optical properties of the nano-columns were investigated using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), cathodoluminescence (CL) and photoluminescence (PL). The Au+Ga alloy droplets were found to be uniformly distributed on silicon surface. Further, SEM image reveals a vertical growth and cylindrical in shape GaN nano-column. The chemical composition of the nano-column, which composed of gallium and nitrogen ions, was estimated by EDX. CL reveals a strong band edge emission from the GaN nano-column. PL spectra show a peak at 365.7 nm with a full-width half maximum (FWHM) of 65 meV which indicates good optical quality GaN nano-column with low dislocation density. Our results suggest that single crystal GaN nano-column can be grown on Au+Ga alloy on silicon substrate with a low dislocation density for better device performances.