Abstract
In this study, silica nanocapsules within silica shell (SNPs) based on an amphiphilic silica precursor polymer – poly (ethylene glycol) substituted hyperbranched polyethoxysiloxane (PEOS-m PEG) was synthesized through a self-assembly method in a fully aqueous with high efficiency. SNPs was homogeneously distributed in waterborne polyurethane to study the influence on the mechanical properties of the nanocomposite as a novel anti-felting agent for wool fabric. The mechanical properties of the nanocomposite anti-felting agent films improved in comparison with the neat polymer. The storage modulus and tensile strength was increased by 143% and 49%, respectively. The novel nanocomposite anti-felting agent was coated on wool fabrics by a pad-dry-cure process. The area shrinkage of the obtained wool fabrics with nanocomposite was 0.8%, much lower than the fabric treated with the same dosage of neat polymer, 4.1%. The warp tensile strength of the wool fabric was increased to 212.2N with lower polymer consumption by 40%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.