Abstract
AbstractThis study explores the feasibility of tribological self‐lubricating over a wide temperature range by doping Si and Sn solid solution components on the A‐sites of Ti3AlC2 to adapt to the severe circumstances. The specimens were sintered at 1450°C for 120 min under a pressure of 30 MPa in a vacuum environment, and their dry sliding tribological capabilities against Al2O3 at temperatures ranging from ambient temperature to 800°C were investigated using a rotational ball‐on‐disk tribo‐tester. The findings demonstrated a constantly decreased friction coefficient of Ti3Al0.8Si0.2Sn0.2C2 throughout the temperature range and admirable antifriction at higher temperatures where wear rates were 1–2 orders of magnitude lower than those at room temperature, which was superior to earlier reported Ti3AlC2. The predominant friction surface self‐adaptability mechanisms after solid solution treatment were determined to be tribo‐oxidation wear and tribo‐chemical reactions that played a vital role by examining the microstructural evolutions and tribo‐chemical phase composition on friction surfaces at various temperatures. The tribo‐oxidation‐induced generated lubricant film consisting of TiO2, Al2O3, SnO2 mixture oxide phases, and aluminosilicates was responsible for the decreased friction coefficient and wear rate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.