Abstract
Healing of impact damage in vascular fiber-reinforced composite beam specimens was explored using a flexure after impact testing protocol. Two-part epoxy and amine based healing agents were delivered to impact-damaged beam specimens using a novel air assisted reagent delivery scheme. The incorporation of microchannels into composite specimens did not alter the flexural stiffness or strength of the composites, however, the post impact flexural strength was reduced, on average, by 25.7%. Flexure testing of healed specimens demonstrated 47% recovery of strength and 83% recovery of moduli when compared to control samples in which no agents were delivered. Optical cross-sectional micrographs reveal that not all damage regions are infiltrated during healing as a result of incomplete damage connectivity. A damage filling efficiency during healing agent infiltration was calculated and was found to positively correlate with recovery of post-impact strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.