Self-healing of cracks formed in Silicon-Aluminum anodes electrochemically cycled at high lithiation rates

Abstract

Abstract Lithiation-induced volume changes in Si result in fracture and fragmentation of Si anodes in Li-ion batteries. This paper reports the self-healing behaviour of cracks observed in micron-sized Si particles dispersed in a ductile Al matrix of a Si-Al electrode electrochemically cycled vs. Li/Li + using a high lithiation rate of 15.6 C. Cross-sectional high-resolution transmission electron microscopy and Raman spectroscopy revealed that an amorphous layer with a depth up to ∼100 nm was formed at the surface of Si particles. In-situ optical microscopy performed during electrochemical experiments revealed development of cracks in Si particles as the voltage decreased to 0.02 V during lithiation. Self-healing of cracks in Si particles occurred in two steps: i) arresting of the crack growth at the Si/Al interface as the surrounding Al matrix had a higher fracture toughness and thus acted as a barrier to crack propagation, and ii) closure of cracks due to compressive stresses applied to the crack faces by the amorphous zones formed on each side of the crack paths.