Abstract
Elastomers with high dielectric permittivity that self‐heal after electric breakdown and mechanical damage are important in the emerging field of artificial muscles. Here, a one‐step process toward self‐healable, silicone‐based elastomers with large and tunable permittivity is reported. Anionic ring‐opening polymerization of cyanopropyl‐substituted cyclic siloxanes yields elastomers with polar side chains. The equilibrated product is composed of networks, linear chains, and cyclic compounds. The ratio between the components varies with temperature and allows realizing materials with largely different properties. The silanolate end groups remain active, which is the key to self‐healing. Elastomeric behavior is observed at room temperature, while viscous flow dominates at higher temperatures (typically 80 °C). The elasticity is essential for reversible actuation and the thermoreversible softening allows for self‐healing and recycling. The dielectric permittivity can be increased to a maximum value of 18.1 by varying the polar group content. Single‐layer actuators show 3.8% lateral actuation at 5.2 V µm–1 and self‐repair after a breakdown, while damaged ones can be recycled integrally. Stack actuators reach an actuation strain of 5.4 ± 0.2% at electric fields as low as 3.2 V µm–1 and are therefore promising for applications as artificial muscles in soft robotics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.