Abstract
The dependence of carrier concentration and mobility profiles on the dose of 400 keV Se ions implanted into Cr-doped semi-insulating GaAs, and on the annealing temperature has been studied for doses ranging from 3 × 10 12/cm 2 to 2 × 10 15/cm 2 and for annealing temperatures between 800 and 1000°C. Sputtered aluminum oxy-nitride and silicon nitride films were used as encapsulants for protection of the implanted surface during annealing treatments. The carrier profiles exhibited deep tails for implantations along both random and {110} planar directions. It was found that annealing temperatures of 900°C or above were necessary to obtain high carrier density and mobility values for implantation doses above 1 × 10 14/cm 2. Samples encapsulated with aluminum oxy-nitride films exhibited 3 to 4 times higher carrier concentration values and also slightly higher mobility values than those encapsulated with silicon nitride films. The maximum carrier concentration obtained was about 4 × 10 18/cm 3 with aluminum oxy-nitride films as the encapsulant.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call