Abstract
A Au-CeO(2) nanocomposite film has been investigated as a potential sensing element for high-temperature plasmonic sensing of H(2), CO, and NO(2) in an oxygen containing environment. The CeO(2) thin film was deposited by molecular beam epitaxy (MBE), and Au was implanted into the as-grown film at an elevated temperature followed by high temperature annealing to form well-defined Au nanoclusters. The Au-CeO(2) nanocomposite film was characterized by X-ray diffraction (XRD) and Rutherford backscattering spectrometry (RBS). For the gas sensing experiments, separate exposures to varying concentrations of H(2), CO, and NO(2) were performed at a temperature of 500 °C in oxygen backgrounds of 5.0, 10, and ∼21% O(2). Changes in the localized surface plasmon resonance (LSPR) absorption peak were monitored during gas exposures and are believed to be the result of oxidation-reduction processes that fill or create oxygen vacancies in the CeO(2). This process affects the LSPR peak position either by charge exchange with the Au nanoparticles (AuNPs) or by changes in the dielectric constant surrounding the particles. Spectral multivariate analysis was used to gauge the inherent selectivity of the film between the separate analytes. From principal component analysis (PCA), unique and identifiable responses were seen for each of the analytes. Linear discriminant analysis (LDA) was also used and showed separation between analytes as well as trends in gas concentration. Results indicate that the Au-CeO(2) thin film is selective to O(2), H(2), CO, and NO(2) in separate exposures. This, combined with the observed stability over long exposure periods, shows the Au-CeO(2) film has good potential as an optical sensing element for harsh environmental conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.