Abstract
Selective laser melting (SLM) additive manufacturing of the SiC/AlSi10Mg composite powder systems with different starting SiC particle sizes was performed to produce in-situ Al4SiC4+SiC hybrid reinforced Al matrix composites. The influence of starting SiC particle size on the constitutional phases, microstructural features, and mechanical properties of the SLM-processed composite parts was studied. As the SiC particle size decreased, the extent of in-situ reaction between aluminum melt and SiC particles was enhanced, leading to the elevated formation of Al4SiC4 reinforcing phase. With the fine SiC particles (D50=5ÎŒm) used, the residual SiC particles with a reduced size of 3ÎŒm were dispersed homogeneously throughout the matrix, thereby enhancing the microstructural homogeneity of the part. With the enhancement of in-situ reaction, the formation of plate-like and particle-structured Al4SiC4 reinforcement was significantly accelerated, favoring the formation of (Al4SiC4+SiC)/Al hybrid reinforced composites after SLM. Using fine SiC particles, the reinforcement/matrix wettability was improved, leading to a nearly full densification level of 97.2% theoretical density of SLM-processed part. The microhardness of 218.5HV0.1 showed at least 50% improvement upon SLM-processed unreinforced AlSi10Mg. The fine SiC particles also reduced the coefficient of friction (COF) by 19% and the wear rate by 66% compared to the SLM part processed with coarse SiC particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.