Abstract
In this study, the processability of the hot work tool steel AISI H10 was investigated using selective laser melting (SLM). The tool steel was fabricated at different process parameters using a substrate plate heating system to prevent cracking. The microstructure was investigated for defects such as cracks, pores, and lack of fusion. Microscopic investigations showed a fine cellular dendritic microstructure in the as-built condition. Due to the high cooling rates in the SLM process and the resulting residual stresses, cracks were found despite substrate preheating. For this reason, the preheating temperature was adapted. Process parameter optimization including the substrate preheating temperature show crack-free tool steel samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.