Abstract
Rhodium (0) nanoparticles were generated in the nanopores of Montmorillonite K-10 clay by reduction of RhCl3·3H2O impregnated clay with NaBH4. Pore size of the clay and hence the size of Rh nanoparticle was controlled by choosing <2μm fraction of the clay as catalyst support. TEM/HRTEM/SAED images confirmed the growth of well dispersed spherical Rh (0) nanoparticles in 1–3nm diameter range having face centred cubic lattice with inter-planar lattice fringe spacing of 0.23nm corresponding to [111] planes. XPS analysis confirmed the presence of Rh metal in zero oxidation state and absence of other oxidation states of Rh. BET surface area determination through N2 adsorption–desorption isotherm revealed decrease in surface area of the clay support from 298m2/g to 196.4m2/g after incorporation of Rh (0) nanoparticles. The Rh (0) nanoparticles supported clay is proved to be highly active and selective heterogeneous catalyst for hydrogenation of monoterpenes (geraniol, limonene, β-pinene, citronellal and linalool) at ambient temperature and pressure (1–4bar). The number of active sites was calculated using surface statistics and adopting model for full shell clusters. Turnover frequency (TOF) calculations for the catalyst gave encouraging results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.