Abstract
The transformation of CO2 into CO through the reverse water gas shift (RWGS) reaction is very sensitive to the metal particle size and metal-support interactions. Indeed, large metallic particles or aggregates tend to produce more methane than CO. In this context, magnetron sputtering deposition was explored here for the preparation of highly dispersed nickel catalyst supported on silica. The Ni catalyst prepared for 30min of sputtering time contains 2.4wt% of Ni, small metal particles size (2.3nm) and controlled composition (77% Ni, 23% Ni oxides). In-situ XANES under RWGS reaction conditions indicates reduction of nickel in the temperature range from 250 to 500°C. The conversion of CO2 into CO through the RWGS reaction was close to the thermodynamic equilibrium values for 1:1 and 1:4 (CO2:H2) gas composition at temperature as high as 800°C. CO was produced continuously for 40h at 660°C without significant drop of activity. The overall catalytic performance was superior to that of a classical catalyst prepared by incipient wetness impregnation, as evidenced by the higher activity at T>600°C and stability for a long time on stream.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.