Abstract

Structural changes of the coordination polymer associated with gas adsorption (gate opening-type adsorption) can be linked to bulk physical properties such as magnetism, electrical conductivity, and dielectric properties. To enable real-space sensing applications, it is imperative to have a system where the selective adsorption of mixed gases can be correlated with physical properties. In this report, we demonstrate that a crystalline sample of one-dimensional (1D) coordination polymer exhibits selective CO2 adsorption while simultaneously displaying dielectric switching behavior in a mixed N2/CO2 gas environment. In the crystal of {[Cu2(2-TPA)4(pz)]·CH3CN}n (1·CH3CN), where 2-TPA and pz are 2-thiophencarboxylate and pyrazine, respectively, paddle wheel-type units of [Cu2(2-TPA)4] are bridged by pz, forming a 1D chain structure. One of the two crystallographically independent 2-TPA units was interacted with the pz moiety of the adjacent 1D chain by π···π interactions, forming a two-dimensional (2D) layer parallel to the ab plane. Activated 1 shows selective CO2 adsorption by a gate opening-type adsorption mechanism, indicating that the CO2 adsorption process is accompanied by a structural change. The change in the real part of dielectric permittivity (ε') under the mixed N2/CO2 gas flow is a result of the selective CO2 adsorption, which was supported by the enthalpy changes (ΔH) associated with CO2 adsorption in two methods: CO2 adsorption isotherms and temperature-dependent measurements of ε' under a mixed N2/CO2 gas flow. The calculated ΔH values were found to be in good agreement across both methods. The CO2 ratio in the mixed N2/CO2 gas flow increased, and the switching ratio of ε' (Δε') also increased. Notably, Δε' exhibited a marked increase beyond the pressure required for gate opening adsorption.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call