Ultrashort pulse lasers have been increasingly gaining importance for the selective structuring of dielectric thin films in industrial applications. In a variety of works the ablation of thin \(\hbox {SiO}_{2}\) and \({\hbox {SiN}}_{x}\) films from Si substrates has been investigated with near infrared laser wavelengths with photon energies of about 1.2 eV where both dielectrics are transparent (\(E_{{\mathrm{gap,SiO}_{2}}}\approx 8\,\hbox {eV}; E_{{\mathrm{gap,SiN}}_{x}}\approx 2.5\,\hbox {eV}\)). In these works it was found that few 100 nm thick \(\hbox {SiO}_{2}\) films are selectively ablated with a “lift-off” initiated by confined laser ablation whereas the \(\hbox {SiN}_{{x}}\) films are ablated by a combination of confined and direct laser ablation. In the work at hand, ultrafast pump-probe imaging was applied to compare the laser ablation dynamics of the two thin film systems directly with the uncoated Si substrate—on the same setup and under identical parameters. On the \(\hbox {SiO}_{2}\) sample, results show the pulse absorption in the Si substrate, leading to the confined ablation of the \(\hbox {SiO}_{2}\) layer by the expansion of the substrate. On the \(\hbox {SiN}_{{x}}\) sample, direct absorption in the layer is observed leading to its removal by evaporation. The pump-probe measurements combined with reflectivity corrected threshold fluence investigations suggest that melting of the Si substrate is sufficient to initiate the lift-off of an overlaying transparent film—evaporation of the substrate seems not to be necessary.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.