Selective extraction of cocaine from biological samples with a miniaturized monolithic molecularly imprinted polymer and on-line analysis in nano-liquid chromatography

Abstract

We report the on-line coupling of a monolithic molecularly imprinted polymer to nano-liquid chromatography for the selective analysis of cocaine and its main metabolite, benzoylecgonine, in complex biological samples. After the screening of different synthesis conditions, a monolithic molecularly imprinted polymer was in situ synthesized into a 100 μm internal diameter fused-silica capillary using cocaine as template, methacrylic acid as functional monomer, and trimethylolpropane trimethacrylate as cross-linker. Scanning electron microscopy was used to assess the homogeneous morphology of the molecularly imprinted polymer and its permeability was measured. Its selectivity was evaluated by nano-liquid chromatography-ultraviolet, leading to imprinting factors of 3.2 ± 0.5 and 2.2 ± 0.3 for cocaine and benzoylecgonine, respectively, on polymers resulting from three independent syntheses, showing the high selectivity and the repeatability of the synthesis. After optimizing the extraction protocol to promote selectivity, the monolithic molecularly imprinted polymer was successfully on-line coupled with nano-liquid chromatography-ultraviolet for the direct extraction and analysis of cocaine present in spiked human plasma and saliva samples. The repeatability of the obtained extraction recovery, between 85.4 and 98.7% for a plasma sample spiked at 100 ng mL−1, was high with relative standard deviation values lower than 5.8% for triplicate analyses on each of the three independently synthesized molecularly imprinted polymers. A linear calibration range was achieved between 100 and 2000 ng mL−1 (R2 = 0.999). Limits of quantification of 14.5 ng mL−1 and 6.1 ng mL−1 were achieved in plasma and urine samples, respectively. The very clean-baseline of the resulting chromatogram illustrated the high selectivity brought by the monolithic molecularly imprinted polymer that allows the removal of a huge peak corresponding to the elution of interfering compounds and the easy determination of the target analyte in these complex biological samples.