Abstract
Selective liquid-phase (LPE) epitaxial growth of InP was performed on patterned Si(1 0 0) substrates. The growth temperature was rapidly cooled, then the crystal growth proceeded at constant temperature. As a result, area-selective epitaxy (ASE) and slight epitaxial lateral overgrowth (ELO) layers were achieved in narrow openings and small nuclei were observed in the wide openings. X-ray diffraction results show that the lattice strain in the InP nuclei on the Si substrate was fully relaxed. Huber etching revealed the dislocation-related etch pits in ASE layers, and it is shown that the etch pit density (EPD) is dependent on the length of open seed area.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.