Abstract
SUMMARYThe corrosion of Zn-Ni alloy coatings in pure and NaHCO, containing Nad solutions was investigated under open circuit potential conditions. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) techniques were applied for the alloy surface characterisation, while direct current plasma emission spectrometry was used for test solution and corrosion product film analysis. It has been established that Zn dissolves preferentially leaving a top layer slightly enriched with Ni. However, this layer does not act as a barrier layer for the further corrosion attack. The presence of NaHCO3, in NaC! solution causes a reduction in the corrosion rales of Zn-Ni alloy and the thickness of corrosion product (oxide) film, as well as affecting the ratio of the soluble and insoluble fractions of ionised Zn and Ni and the development of the surface morphology. In a pure NaCl solution Zn-Ni corrosion occurred with surface roughening, while in the presence of NaHCO3 the process was accompanied by surface smoothing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.