Selective area deposited n-Al0.5Ga0.5N channel field effect transistors with high solar-blind ultraviolet photo-responsivity

Abstract

We report on AlGaN field effect transistors over AlN/sapphire templates with selective area grown n-Al0.5Ga0.5N channel layers for which a field-effect mobility of 55 cm2/V-sec was measured. Using a pulsed plasma enhanced chemical vapor deposition deposited 100 A thick SiO2 layer as the gate-insulator, the gate-leakage currents were reduced by three orders of magnitude. These devices with or without gate insulators are excellent solar-blind ultraviolet detectors, and they can be operated either in the photoconductive or the photo-voltaic modes. In the photo-conductive mode, gain arising from hole-trapping in the depletion region leads to steady-state photoresponsivity as high as 1.2 × 106A/W at 254 nm, which drops sharply below 290 nm. A hole-trapping limited detector response time of 34 ms, fast enough for real-time flame-detection and imaging applications, was estimated.