This study tested the effect of cryogenic treatment on nickel-titanium (NiTi) endodontic instruments. Ten rotary NiTi instruments (ProFile 30, 0.06; Dentsply Maillefer Instruments SA, Baillegues, Switzerland)) were subjected to deep dry cryogenic treatment at liquid nitrogen temperature (−185°C) (group A) and compared with that of nontreated instruments (group B). Root canals of 30 extracted permanent mandibular premolars were prepared to size 25 using ProFile 0.04 taper rotary NiTi instruments. Each instrument was used in 4 root canals for a total of 240 seconds. Cutting efficiency in rotary motion was assessed from weight loss of tooth samples after instrumentation. Wear resistance was assessed from surface defects on cutting heads pre- and postinstrumentation using scanning electron microscope. The weight loss was significantly higher in group A (p < 0.05, Student t test). The presence of surface defects after use was higher in group B. Deep dry cryogenic treatment increases the cutting efficiency significantly but not the wear resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.