Preventing corrosion in the steel reinforcement of concrete structures is crucial for maintaining structural integrity and load-bearing capacity as it directly impacts the safety and lifespan of concrete structures. By preventing rebar corrosion, the durability and seismic performance of the structures can be significantly enhanced. This study investigates the hysteresis behavior of both corroded and non-corroded engineered cementitious composite (ECC)-glass-fiber-reinforced polymer (GFRP) spiral-confined reinforced-concrete (RC) columns. Employing experimental methods and finite element analysis, this research explores key seismic parameters such as crack patterns, failure modes, hysteretic responses, load-bearing capacities, ductility, stiffness degradation, and energy dissipation. The results demonstrate that ECC-GFRP spiral-confined RC columns, compared to traditional RC columns, show reduced corrosion rates, smaller crack widths, and fewer corrosion products, indicating superior crack control and corrosion resistance. Hysteresis tests revealed that ECC-GFRP columns, at a 20% target corrosion rate, exhibit an enhanced load-bearing capacity, ductility, and energy dissipation, suggesting improved durability and seismic resilience. Parametric and sensitivity analyses confirm the finite element model's accuracy and highlight the significant influence of concrete compressive strength on load-bearing capacity. The findings suggest that ECC-GFRP spiral-confined RC columns offer promising applications in coastal and seismic-prone regions, enhancing corrosion resistance and mechanical properties, thus potentially reducing formwork costs and improving construction quality and efficiency.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.