Abstract
Microstructural heterogenity was examined in the as-cast microstructure of directionally solidified ZS 26 nickel based superalloy. The distribution of elements in primary and secondary dendrite growth direction was determined by quantitative EDX analysis. Measurements of elemental partitioning show apparent segregation behaviour of Al, Ti, W, and Ni during solidification. The series of one stage solution were used to homogenize samples microstructure of samples and simultaneously to study the solutes redistribution
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.